The Inverted Hysteresis Loops and Exchange Bias Effects in Amorphous/Nanocrystalline Fe72Cu1V4Si15B8 Ribbons at Room Temperature

  • Radoslav Surla Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Faculty of Technical Sciences Čačak, University of Kragujevac
  • Nebojša Mitrović Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Faculty of Technical Sciences Čačak, University of Kragujevac
  • Milica Vasić Faculty of Physical Chemistry, University of Belgrade
  • Dragica Minić Faculty of Physical Chemistry, University of Belgrade

Abstract

Тhe influence of thermally induced microstructural transformations on magnetic properties of Fe72Cu1V4Si15B8 ribbon with combined amorphous/nanocrystalline structure is presented. The experiments showed that thermally induced structural changes are in correlation with the appearance of magnetic hysteresis, i.e. with inverted hysteresis loops (IHL) and exchange bias (EB) effects. It was found that the ratio of surface to volume of a ribbon sample have an influence on hysteresis loop appearance. The inverted hysteresis loops were observed for the 1.5 mm wide and 55 μm thick alloy samples shorter than 10 mm, but for the samples longer than 10 mm hysteresis loops were normal. With an increase of annealing temperature, a shift of the hysteresis loops measured at room temperature was noticed. The highest positive exchange bias field Heb was observed for the sample annealed at 723 K, together with the lowest magnetic field at which the changes from inverted to normal hysteresis loop occurred. Annealing at the temperature of 823 K resulted in negative Heb.

Published
2020-08-05
Issue
Vol 52 No 3 (2020)
Section
Articles

Copyright 

Authors retain copyright of the published article and have the right to use the article in the ways permitted to third parties under the Creative Commons Attribution 4.0 International license. Full bibliographic information (authors, article title, journal title, volume, issue, pages) about the original publication must be provided and a link must be made to the article's DOI. This license allows to copy and redistribute the material in any medium or format, remix, transform, and build upon it for any purpose, even commercially, as long as appropriate credit is given to the original author(s), a link to the license is provided and it is indicated if changes were made.