Effect of Sintering on the Piezoelectric Properties and Microstructure of Lead Free (Ba1-xCaxZr0.1Ti0.9O3) (x = 0.065) Ceramics
Abstract
In this work, pellet samples of barium calcium zirconate titanate (Ba1-xCaxZr0.1Ti0.9O3, x=0.065) were prepared using solid state reaction route with double sintering. The structural and piezoelectric properties were measured. Further, SEM and EDAX analysis were observed. With different sintering temperature, the density and grain size of the prepared pellet samples were changed and further, their effect in piezoelectric properties has been observed. For the prepared samples, the converse piezoelectric constant (d33*) has been decreased with the increase in sintering temperature. The piezoelectric constant (d33*) was measured highest (153 pm/V) at 1300oC.
Copyright
Authors retain copyright of the published article and have the right to use the article in the ways permitted to third parties under the Creative Commons Attribution 4.0 International license. Full bibliographic information (authors, article title, journal title, volume, issue, pages) about the original publication must be provided and a link must be made to the article's DOI. This license allows to copy and redistribute the material in any medium or format, remix, transform, and build upon it for any purpose, even commercially, as long as appropriate credit is given to the original author(s), a link to the license is provided and it is indicated if changes were made.