The Influence of Sintering Condition on Microstructure, Phase Composition, and Electrochemical Performance of the Scandia-Ceria-Co-Doped Zirconia for SOFCs
Abstract
Samples of 6 mol% Sc2O3 - 1 mol% CeO2 co-doped ZrO2 were fabricated by conventional ceramic processing methods and sintered at various temperatures from 1000 to 1650°C in air. The sintering conditions on microstructure and phase content are investigated using various characterization methods, including pycnometry, diffraction, and spectroscopy. The electrical conductivity of samples was investigated using electrochemical impedance spectroscopy (EIS). The effect of inductive load (measured from room temperature to 800°C) is discussed in low to high temperature regimes. At T less than 400°C since the arc is not a complete semicircle, the high-frequency arc could be fit using a constant phase element (CPE), while by subtraction of inductive load, a good fit is achieved using a capacitor element instead of CPE. The Arrhenius conductivity plot of samples reveals that the specimen sintered at 1600°C for 6 hours exhibits the highest conductivity. The activation energy (Ea) and conductivity pre-exponential (σ0) factor are calculated from a linear fit to data that decreases by the increase in sintering temperature.
Copyright
Authors retain copyright of the published article and have the right to use the article in the ways permitted to third parties under the Creative Commons Attribution 4.0 International license. Full bibliographic information (authors, article title, journal title, volume, issue, pages) about the original publication must be provided and a link must be made to the article's DOI. This license allows to copy and redistribute the material in any medium or format, remix, transform, and build upon it for any purpose, even commercially, as long as appropriate credit is given to the original author(s), a link to the license is provided and it is indicated if changes were made.