The Influence of Compaction Pressure on the Density and Electrical Properties of Cordierite-based Ceramics
Abstract
Due to its characteristics, cordierite, 2MgO⋅2Al2O3⋅5SiO2, is a high-temperature ceramic material of a great scientific interest. Mechanical activation of the starting mixtures containing 5.00 mass% TiO2 was performed in a high-energy ball mill for 10 minutes. The compaction pressure varied from 0.5 to 6tcm-2 (49–588 MPa). The sintering process was performed at 1350ºC for four hours in the air atmosphere. The phase composition of the activated and sintered samples was analyzed using X-ray diffraction. Scanning electron microscopy was used to analyze the microstructure of both compacted and sintered samples. The authors have investigated the influence of compaction pressure on the sintered samples and their electrical properties.
Copyright
Authors retain copyright of the published article and have the right to use the article in the ways permitted to third parties under the Creative Commons Attribution 4.0 International license. Full bibliographic information (authors, article title, journal title, volume, issue, pages) about the original publication must be provided and a link must be made to the article's DOI. This license allows to copy and redistribute the material in any medium or format, remix, transform, and build upon it for any purpose, even commercially, as long as appropriate credit is given to the original author(s), a link to the license is provided and it is indicated if changes were made.