The Effect of Aging Temperature and Aging Duration on the Dry Sliding Wear Behavior of Ti6Al4V Alloy
Abstract
In this study, Ti6Al4V (Grade 5) alloys were first dissoluted at 850ºC for 120 min and then were aged at 250, 350, 450, 550, 650, and 750ºC, respectively. After each aging duration (by looking at hardness ratios aged between 9 to 54 hours), the hardness of the samples was measured. Depending on the aging temperature and time increase, hardness increased upon the formation of θ' phases. After the formation of θ' phases, the hardness started to decrease. The highest hardness value was measured in the sample aged at 450ºC for 24 hours. The wear behavior of the untreated and the aged samples was investigated through a detailed pin-on-disc test. The effect of the aging temperature on the volume loss, the specific wear rate, and the coefficient of friction were examined. Metallographic analyses were performed before and after the wear tests. Both abrasive and adhesive wear formations were observed on the FESEM-EDS images of the worn surfaces. When the results were evaluated, it was observed that the highest hardness and good wear behavior were obtained for the samples aged at 450ºC for 24 hours.
Copyright
Authors retain copyright of the published article and have the right to use the article in the ways permitted to third parties under the Creative Commons Attribution 4.0 International license. Full bibliographic information (authors, article title, journal title, volume, issue, pages) about the original publication must be provided and a link must be made to the article's DOI. This license allows to copy and redistribute the material in any medium or format, remix, transform, and build upon it for any purpose, even commercially, as long as appropriate credit is given to the original author(s), a link to the license is provided and it is indicated if changes were made.