Effect of Sintering Temperature on the Mechanical Properties of Vacuum Sintered Co-(Zn)-Ni-Al Alloys

Authors

  • G. Johnsy Arputhavalli Department of Physics, Coimbatore Institute of Technology
  • S. Agilan Department of Physics, Coimbatore Institute of Technology
  • S. Jebasingh Department of Mathematics, Karunya Institute of Technology and Sciences
  • S. Vijay Joseph Department of Mechanical Engineering, Karunya Institute of Technology and Sciences

Abstract

In the present study, the wear resistance behavior and the microhardness of the Co38Ni35Al27 and Co35Zn10Ni32Al23 ferromagnetic shape memory alloys (FSMAs) were investigated. The alloy samples were prepared by powder metallurgy method along with the vacuum sintering technique. The major aim is to prepare an alloy with high wear resistance having remarkable microhardness suitable for the sustainable shape memory alloy. The wear test report shows that the wear resistance is high for the sample sintered at 673 K and it gradually reduces when the sintering temperature decreases. The result also shows that the inclusion of zinc in the alloy increases the wear rate. The maximum hardness value of 126 HV was observed in Co38Ni35Al27 sample sintered at 673 K for 8 hrs because of its minimal porosity.

Downloads

Published

2020-08-05

Issue

Vol. 52 No. 3 (2020)

Section

Articles

License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Authors retain copyright of the published papers and grant to the publisher the right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media. Articles will be distributed under the Creative Commons Attribution International License (CC BY 4.0).