The Effect of Acrylate on the Properties and Machinability of Alumina Ceramics

Authors

  • Maja Kokunešoski Institute of Nuclear Sciences Vinča, National Institute of the Republic of Serbia, University of Belgrade
  • Đorđe Janaćković Faculty of Technology and Metallurgy, University of Belgrade
  • Dušan Kićević Institute of Nuclear Sciences Vinča, National Institute of the Republic of Serbia, University of Belgrade
  • Svetlana Ilić Institute of Nuclear Sciences Vinča, National Institute of the Republic of Serbia, University of Belgrade
  • Aleksandra Šaponjić Institute of Nuclear Sciences Vinča, National Institute of the Republic of Serbia, University of Belgrade

Abstract

Effect of methyl methacrylate (MMA) as a binder and heating treatment were investigated to improve green alumina compacts machinability. Properties of green compacts and their corresponding sintered samples prepared with and without MMA were compared. Investigation of green and sintered properties was performed on samples compacted at applied pressures up to 150 MPa. After pressing, samples with MMA were thermally treated at 115oC. The intention was to enhance the polymerization of MMA at a temperature a little higher than the glass transition temperature (Tg = 103oC) of poly (methyl methacrylate). Green compacts with MMA had higher green density values than those without MMA. Sintered samples with MMA had lower values of sintered density and higher values of total porosity; after sintering, relative linear shrinkage was around 15 % for the whole range of applied pressures. The possibility of easily machining the green compacts with MMA produces great possibilities for application in many fields.

Downloads

Published

2023-03-15

Issue

Vol. 55 No. 1 (2023)

Section

Articles

License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Authors retain copyright of the published papers and grant to the publisher the right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media. Articles will be distributed under the Creative Commons Attribution International License (CC BY 4.0).